Effect of Silica Product Content on Compaction Test of the Nano-Soil-Cement

Soil cement is a mixture of Portland cement, soil and water, in which hydration of cement and compaction causes the materials’ constituents to bond together making a dense and durable composition with low permeability and abrasion resistant. Since most of the recent researches are focused on the addition of nano-SiO۲ on concrete, in this paper it has been attempted to use nano-SiO۲ particles in soil-cement and observe the effects. Due to the fact that in concrete there are no particles passing sieve ۲۰۰ and this restriction does not apply to soil-cements, some tests were carried out on the nano-SiO۲ + soil-cement matrix because of the meaningful difference between concrete and soil-cement. The test procedure consists of moisture-dry density. In these tests, silica fume (with specific surface area of ۲۱ m۲/g), nano-SiO۲ (with specific surface area of ۲۰۰ and ۳۸۰ m۲/g) were added to soil-cement. The results show that adding type of nano-SiO۲ particles to the soil-cement with optimum amount of silica content can improve the compaction of soil cement.

کلیدواژه ها:

Soil-cement ، optimum amount ، Compaction Test ، Nano-SiO۲.