Effect of Accumulative Roll Bonding Process on Mechanical Properties of Al-Based Composite Reinforced with Nano-Trioxide Tungsten

In the present study, an Al/WO۳p metal matrix nanocomposite was fabricated by accumulative roll bonding(ARB) technique. Mechanical properties of specimens were investigated by microhardness and tensile test.Several factors that affect uniform distribution particles were investigated. After ۱۲ ARB cycles, ananocomposite with a uniform distribution of nanoparticles was produced. It was shown that the tensilestrength of the ARBed composite enhanced with the increasing number of ARB cycles. After the first cycle, asignificant increase was observed in the tensile strength of nanocomposite in ۲.۰ percent volume of WO۳p,from ۸۹ MPa to ۱۲۸ MPa (almost ۱.۴ times increase in strength). After the final cycle, the tensile strengthvalue increased to ۲۰۵ MPa (that is almost ۲.۳ times increase in strength) due to the strain hardening and grainrefinement. The X-ray diffraction results showed that Al/WO۳p nanocomposite with the average crystallitesize of ۴۱ nm was successfully attained after ۱۲ cycles of the ARB process. Finally, observations revealed thatthe fracture mode in Al/WO۳p nanocomposite was of type shearing ductile fracture with elongated shallowdimples.

کلیدواژه ها:

Accumulative Roll Bonding ، Nanocomposite ، Microstructure ، Mechanical Properties