Effects of Equal Channel Angular Pressing (ECAP) Process with an Additional Expansion-Extrusion Stage on Microstructure and Mechanical Properties of Mg–۹Al–۱Zn
محل انتشار: فصلنامه مواد پیشرفته و فرآوری، دوره: 9، شماره: 4
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 241
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-9-4_005
تاریخ نمایه سازی: 4 تیر 1401
چکیده مقاله:
In this study, equal channel angular pressing (ECAP) process with an additional expansion-extrusion stage named expansion-extrusion equal channel angular pressing (EECAP) process is utilized for producing bulk ultrafine grained (UFG) Mg–۹Al–۱Zn magnesium alloy. In this process, cyclic expansion-extrusion (CEE) and equal channel angular pressing (ECAP) processes are combined. AZ۹۱ magnesium alloy was used for this experiment. An FEM simulation was performed to calculate the compressive hydrostatical stress. Furthermore, microstructural and mechanical properties were investigated. The experimental findings revealed that the ductility of the sample remains almost constant (۰.۰۳% drop) while ultimate tensile strength increased about ۳۰%. The average value of microhardness improved from ۴۸ Hv to ۶۵ Hv (۳۵%) and grain size refined from ۱۴۴ µm to ۳.۴ µm. Despite the expansion part of the die, there is no need for back pressure. Another advantage of this new method is maintaining ductility while strengthening.
کلیدواژه ها:
نویسندگان
Mahnoush Rassa
Department of Mechanical Engineering, College of Engineering, University of Tehran, Tehran, Iran
Geonik Azadkoli
Department of Mechanical Engineering, College of Engineering, University of Tehran, Tehran, Iran
Mohammad Eftekhari
Department of Mechanical Engineering, College of Engineering, University of Tehran, Tehran, Iran
Ali Fata
Department of Mechanical Engineering, Faculty of Engineering, University of Hormozgan, Bandar Abbas, Iran
Ghader Faraji
Department of Mechanical Engineering, College of Engineering, University of Tehran, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :