Detecting compressive strain by evaluation of Raman spectroscopy of the multiwall Carbon nanotubes/TiO۲ nanocomposites
محل انتشار: مجله بین المللی ابعاد نانو، دوره: 11، شماره: 2
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 192
فایل این مقاله در 9 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJND-11-2_007
تاریخ نمایه سازی: 17 خرداد 1401
چکیده مقاله:
Functionalized Multi-walled carbon nanotubes (f-MWCNTs) which are modified using nitric acid and sulfuric acid were evaluated to synthesize a uniform nanocomposite via application of TiO۲. The f-MWCNTs-TiO۲ nanocomposites have been produced via using the chemical simple two-step method. To characterize the structural analysis, scanning electron microscopy (SEM) imaging, ultraviolet-visible (UV-Vis) spectroscopy, and Raman spectroscopy were utilized. The maximum shift of D, G, and ۲G-bands of f-MWCNTs were related to ۲۰ wt. % f-MWCNTs in TiO۲ nanoparticles. Moreover, an up-shift of ۴۰ cm-۱ was recorded for the MWCNTs (G’-band) for ۵ wt. % f-MWCNTs. For ۲۰ wt. % f-MWCNTs/TiO۲ (G-band) nanocomposites, was determined by ۴.۷%. By increasing the amount of f-MWCNTs in f-MWCNs/TiO۲ nanocomposite, the compressive strain was increased. Among the four bonds, the G’-band behaved differently against increasing f-MWCNTs. The shifting frequency of G-band indicates the strong interaction between f-MWCNTs and TiO۲ nanoparticles. The interaction between f-MWCNTs and TiO۲ nanoparticles identified by the Gruneisen parameter. Therefore, a mechanism generated for stress transfer at the interface between f-MWCNTs and TiO۲ nanoparticles which is indicated in many significant increases obtained in the mechanical and acoustical properties.
کلیدواژه ها:
نویسندگان
Marzieh Naddafan
Department of Physics, Shahid Rajaee Teacher Training University, Tehran, Lavizan, P. O. Box ۱۶۷۸۸-۱۵۸۱۱, I. R. Iran.
Ammar Shaker Alattar
Department of Physics, University of Mustansiriyah, Baghdad, IQ, Iraq.
Zahra Dehghani
Department of Physics, University of Neyshabur, Neyshabur, P. O. Box ۹۳۱۹۷۷۴۴۰۰, I. R. Iran.
Rasoul Malekfar
Atomic and Molecular Physics Group, Faculty of Basic Sciences, Tarbiat Modares University, Tehran, P. O. Box ۱۴۱۱۵-۱۷۵, I. R. Iran.
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :