چکیده مقاله:
This study aims to fabricate an optimum interface surface for intracochlear catheter applications. The samples were first fabricated of two-component liquid dimethyl siloxane by designing and fabricating a mold, and then the assembly underwent surface treatment using a plasma irradiation device. The water contact angle test results showed an increase in the surface hydrophilicity of this material that water drop contact angle of origin silicone is ۱۰۵° that after treatment decrease to ۶۰°, which has the property of reducing the effect of cellular cutting in the inner ear when passing through the scala tympani. The surface engagement during passage was also minimized with an increase in surface roughness at the nanoscale. SEM and AFM photomicrographs and nano graphs show that the morphology of catheter surface in nanoscale changed and roughness increased, which is desirable for this purpose. The cell viability test results showed an improved adhesion and cell growth on the modified surface and origin silicone, and ۹۵ % viability of cells confirmed, indicating the optimal biocompatibility of the modified silicone sample. This catheter can be used in cochlear implantation and drug delivery before surgery to enhance therapeutic efficiency
کلیدواژه ها:
نویسندگان
Mohammad Ajal-Louian
New Hearing Technologies Research Center, Baqiyatallah University of Medical Sciences; Tehran, Iran
saeed golparvaran
Department of Otorhinolaryngology, School of Medicine, Tehran University of Medical Sciences, Tehran, Iran
Hamid Mirzadeh
Department of Biopolymer, Faculty of Polymer Engineering, Amir Kabir University of Technology, Tehran, Iran
Mohammad T. Khorasani
Department of Biocompatible Polymers, Iran Polymer and Petrochemical Institute (IPPI), Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :