Nano, micro and multiscale filler-reinforced functionalized polypropylene composites: FTIR characterization and mechanical study
محل انتشار: فصلنامه پلی اولفین ها، دوره: 9، شماره: 1
سال انتشار: 1401
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 110
فایل این مقاله در 11 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_POJ-9-1_004
تاریخ نمایه سازی: 28 دی 1400
چکیده مقاله:
Nano, micro and hybrid filler-reinforced polypropylene (PP) composites were prepared via melt compounding technique using a twin screw extruder. The nano scale MWCNTs and micro scale glass fibers were used as reinforcements. In addition to the individual effect of nano and micro scale reinforcements in virgin PP, the dual effect of multiscale (MWCNT/glass fiber) fillers was also elucidated. Morphological images revealed the effectiveness of dispersion of the fillers in the matrix and it was observed that the functionalized composites showed increased filler dispersion. The static mechanical properties of the non-functionalized and functionalized samples were compared and the hybrid composite with ۲ wt.% MWCNTs showed the highest tensile strength without modulus reduction. The strong bonding between carboxyl-treated MWCNTs and maleic anhydride-grafted PP was well revealed in the FTIR spectra. In hybrid composites, the effect of silane-treated glass fibers was revealed and the siloxane linkages occurred between the glass fiber surface and silanol groups were confirmed by the FTIR spectra.
کلیدواژه ها:
نویسندگان
Nanoth Rasana
Department of Chemical Engineering and Materials Science, Amrita School of Engineering, Coimbatore, Amrita Vishwa Vidyapeethaam, Coimbatore, India
Karingamanna Jayanarayanan
Department of Chemical Engineering and Materials Science, Amrita School of Engineering, Coimbatore, Amrita Vishwa Vidyapeetham, India
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :