Fabrication of a biopolymer fibrous scaffold for nerve tissue engineering
محل انتشار: کنفرانس بین المللی فرآورش پلیمرها
سال انتشار: 1390
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,207
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
PPSRC2011_222
تاریخ نمایه سازی: 30 بهمن 1390
چکیده مقاله:
Nerve tissue engineering is one of the most promising methods in nerve tissue regeneration. The development of collagen scaffolds can potentially be used in many soft tissue engineering applications. Electrospinning is a polymer processing technique that utilizes an electric field to form fibers from a polymer solution or melt and allows the fabrication of nanofibrous non-woven structures. In this study an attempt was made to develop aligned and random electrospun, nanofibrous scaffolds using collagen. Different parameters in electrospinning process such as solution viscosity, electric field strength, solution flow rate and nozzle to target distance were assessed and optimized to achieve the appropriate scaffold characteristics. To analyze the effect of solution viscosity on fiber diameter, electrospinning was performed using 18, 15, 10 and 7% w/v concentrations. In order to detect the effect of electric field strength, three different experiments were run with electric field strength of 20, 15 and 10 kV, while the other parameters were kept unchanged. Regarding the adjusted electric field, three solution flow rates of 0.2, 0.5 and 0.7 ml/h were set for solution flow rate. Nozzle to target distance parameter was also assessed through three experiments with three distances of 13, 15 and 20 cm. The effects of all these four parameters were traced through the SEM micrographs.
کلیدواژه ها:
نویسندگان
Farzad Yousefi Gharebaghi
Faculty of Biomedical Engineering, Amirkabir University of Technology, ۴۲۴ Hafez Ave
Azadeh Timnak
Faculty of Biomedical Engineering, Amirkabir University of Technology, ۴۲۴ Hafez Ave
Seyed Hajir Bahrami
Faculty of Textile Engineering, Amirkabir University of Technology, ۴۲۴ Hafez Ave
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :