Investigation of ECAR Routes on Mechanical Properties of Explosive-Welded Al-Cu Bimetal
سال انتشار: 1393
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 184
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_MPMPJ-3-4_006
تاریخ نمایه سازی: 23 مهر 1400
چکیده مقاله:
Equal channel angular rolling (ECAR) is a severe plastic deformation method that covered plastic deformation of sheets. In this study, effects of ECAR route shave been investigated on the mechanical and microstructure properties of explosive-welded Al-Cu bimetal. At first, the explosive welding process has been performed to prepare the Al-Cu bimetals. Then, to relieve the stress and preparing of samples for ECAR process, the annealing process of the samples was done. Finally, the ECAR process was performed on the samples in two routes A and C. Results showed that yield and tensile strengths and micro hardness of ECARed samples significantly increased with increasing the number of passes, whereas their ductility decreased. The yield strength of bimetals has been increased from ۸۰ MPa to ۱۰۰ MPa and ۱۳۰ MPa at the routes A and C, respectively. Also, with increasing the number of ECAR passes, the grain size of the ECARed bimetals decreased to about ۲μm.
کلیدواژه ها:
نویسندگان
Mohammad Honarpisheh
Faculty of Mechanical Engineering, University of Kashan, Kashan, Iran
Mahdi Dehghani
Faculty of Engineering, Najafabad branch, Islamic Azad University
Sina Ghaffari
Faculty of Mechanical Engineering, University of Kashan, Kashan, Iran