Nanoporous anodized aluminum thickness optimization through pulse current mode
محل انتشار: فصلنامه مواد پیشرفته و فرآوری، دوره: 3، شماره: 4
سال انتشار: 1394
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 220
فایل این مقاله در 14 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-3-4_002
تاریخ نمایه سازی: 13 مهر 1400
چکیده مقاله:
The purpose of this study was to optimize the thickness of anodizing Aluminum coatings processed under pulse current mode through the Design of Experiments (DOE) method. Thickness measurement, polarization and electrochemical impedance spectroscopy were employed to take Thickness and corrosion behaviors of the anodized coatings into consideration. Also, Field-emission scanning electron microscopy (FE-SEM) was utilized to characterize the surface morphology of the coatings. It was found that the thickness of anodized coatings strongly depends on various parameters among which, time, temperature and pulse current parameters such as current density limit, frequency and duty cycle were considered in the present study. Analysis of variance (ANOVA) was used for estimating the coating thickness. Experimental results showed the maximum value for coating thickness was ۶۲ µm being attained at the maximum and minimum current density of ۶.۲۸ and ۱.۵۵ A/dm۲, a frequency of ۱۵۰.۵ Hz, time of ۵۱ min, duty cycle of ۸۱.۵% and the bath temperature of ۱۳.۵ oC. Also, FE-SEM observation of the surface of anodized coatings showed that this optimum condition leads to a lower porosity amount. Polarization measurements showed that this lower porosity amount caused an increase in corrosion resistance of anodized coatings.
کلیدواژه ها:
نویسندگان
Iman Mohammadi
Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box ۱۱۱۵۵–۹۴۶۶, Azadi Ave, Tehran, Iran
Abdollah Afshar
Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box ۱۱۱۵۵–۹۴۶۶, Azadi Ave, Tehran, Iran
Shahab Ahmadi
Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box ۱۱۱۵۵-۹۴۶۶, Azadi Ave., Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :