Evaluation of Photocatalytic Activity of Fe Doped TiO۲ Thin Film Prepared by sol-gel hot dip-coating

The application of Fe–TiO۲ photocatalysis using sol–gel method by hot–dipping technique was investigated. Then, the influences of fabrication parameters, molar ratios of Fe to TiO۲, the sol temperature, poly ethylene glycol (PEG) content and the number of dipping cycles on the photocatalytic activity in visible light region were mainly studied. The experimental results revealed the sample with the molar ratios of Fe to TiO۲: ۰.۰۱۵, the sol temperature: ۷۰ °C, PEG content: ۲ wt. % and the number of dipping cycles: ۵ showed the best result. The photodegradation efficiency of this sample after ۲ h visible light irradiation increased up to ۸۰% and no crack was detected on the surface of the thin film. When the sol temperature increased from ۲۵ to ۷۰ ºC (the boiling point of the sol), its viscosity increased due to the existence of PEG via forming cross linkage. This phenomenon caused to change the microstructure and improve in optical properties.

کلیدواژه ها:

Fe doped TiO۲ ، Thin film ، Photocatalytic Properties ، hot–dip coating ، Sol–gel