Synthesis of zinc aluminate (ZnAl۲O۴) by mechanochemical processing with different molar ratios of ZnS:Al
محل انتشار: فصلنامه مواد پیشرفته و فرآوری، دوره: 8، شماره: 1
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 173
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_JMATPR-8-1_002
تاریخ نمایه سازی: 9 مرداد 1400
چکیده مقاله:
Zinc aluminate spinel structure (ZnAl۲O۴) was synthesized from mixtures of zinc sulfide (with sphalerite structure) and aluminum. The starting materials with different molar ratios were milled for ۳ hours. The as-milled powders were heated isothermally at ۸۰۰ ⁰C under an air atmosphere for one hour. The heated samples finally were washed out with diluted sulfuric acid and the remained residuals were dried at ۱۱۰ ℃ for two hours. The results showed that aluminium content and the molar ratios of ZnS:Al in the starting materials have significant effect on the formation of ZnAl۲O۴.The as-milled results showed that although the reduction of ZnS by aluminum occurred during milling, the reaction was not completed with increasing the Al content in the starting materials. Except the molar ratio of ۱:۲, no signs of un-reacted Al were observed in other mixtures of ZnS-Al after milling for three hours. The XRD patterns and FT-IR spectra of the acid treated sample revealed that zinc aluminate could be synthesized from mixtures of ZnS-Al and the ZnS-Al mixture with molar ratio of ۴:۲ was the best among all mixtures.
کلیدواژه ها:
نویسندگان
Niloofar Ghani Kolahloo
Materials Engineering Department, School of Engineering, Yasouj University, Yasouj, ۷۵۹۱۸-۷۴۸۳۱, Iran
Nader SETOUDEH
Materials Engineering- School of Engineering-Yasouj University-Yasouj - Iran
Abbas Mohassel
Materials Engineering Department, School of Engineering, Yasouj University, Yasouj, ۷۵۹۱۸-۷۴۸۳۱, Iran
Raziye Hayati
Materials Engineering Department, School of Engineering, Yasouj University, Yasouj, ۷۵۹۱۸-۷۴۸۳۱, Iran
Mohammad Sajjadnejad
Materials Engineering Department, School of Engineering , Yasouj University, Yasouj, ۷۵۹۱۸-۷۴۸۳۱, Iran