Experimental Study on Surface Roughness and Flatness in Lapping of AISI ۵۲۱۰۰ Steel
سال انتشار: 1395
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 168
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_ADMTL-9-2_008
تاریخ نمایه سازی: 18 اردیبهشت 1400
چکیده مقاله:
Lapping is one of the most important polishing processes which can be used to fabricate flat and smooth surfaces. In this paper, the effect of lapping characteristics and mesh number of abrasive particles are studied on the surface roughness and flatness for the machining of hardened AISI ۵۲۱۰۰ rings. The most significant lapping characteristics are pressure, lap plate speed and time. Scanning electron microscopy and optical microscopy are used to investigate micro cracks and surface textures. Results showed that surface roughness increased by rising the lapping pressure and plate speed. Also, reduction of the lapping time and mesh number of abrasive particles led to lower surface roughness. Application of lapping process decreased the flatness to ۱.۲ µm and surface roughness (Ra) from ۰.۵۸ to ۰.۰۵۱ µm. The lapping pressure was a significant factor on the surface roughness; and the lapping time was a significant factor on flatness. However, surface roughness increased with rising of mesh number and lapping time, and increased with decreasing the lapping pressure. The minimum surface roughness was ۰.۰۵۱ μm which was obtained in lapping pressure of ۷ kPa, lapping speed of ۰.۱۶۴ m/s, time of ۱۵ min and mesh number of ۶۰۰.The flatness decreased with lapping speed, and reduced with increasing the pressure, mesh number and lapping time.
کلیدواژه ها:
نویسندگان
Masoud Farahnakian
Faculty of Engineering, Mechanical Engineering Department Najafabad branch, Islamic Azad University, Iran
H. Shahrajabian
Faculty of Engineering, Mechanical Engineering Department Najafabad branch, Islamic Azad University, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :