Synthesis and Characterization of Photocatalytic Activity of Hematite/ Cobalt Oxide/ Graphite Nanocomposites
محل انتشار: ماهنامه بین المللی مهندسی، دوره: 34، شماره: 1
سال انتشار: 1400
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 203
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-34-1_020
تاریخ نمایه سازی: 6 اردیبهشت 1400
چکیده مقاله:
In this study, at first step nanopowder particles of α-Fe۲O۳ (Hematite) and Co۳O۴ were synthesized separately thorough simple chemical method from an aqueous solution of iron (III) nitrate nonahydrate (Fe(NO۳)۳.۹H۲O) and cobalt (II) nitrate hexahydrate (Co(NO۳)۲.۶H۲O) as precursors. After that, three composites from synthesized nanopowders of Fe۲O۳ with ۸, ۱۶ and ۲۴ wt.% of Co۳O۴ were prepared. Graphite nanopowder was added to one composition of samples in weight percentages of ۱.۱۷ and ۲.۳۵. The composition and morphology of the composites were investigated by XRD and FE-SEM, respectively. FE-SEM analysis showed that the morphology of the powders and composites were all spherical in nanoscale. The photocatalytic activity of the composites was examined by measuring the photo-degradation of the aqueous solution of methylene blue under simulated solar light. To determine the photo catalytic activity, the degradation of methylene blue (MB) in the absence of light (dark test) was taken as well. Results showed that addition of Co۳O۴ to Fe۲O۳ decrease the activity of photo-catalytic process while nano-graphite enhanced photo-catalytic process by upward of ~۲ % with respect to the composite without graphite nanoparticles. Stoichiometric calculations showed that the amount of hydrogen produced by water by the composite of Fe۲O۳-۱۶% Co۳O۴- ۲.۳۵% Graphite nanoparticles was ۲۷ μmol H۲/h.g under solar light irradiation.
کلیدواژه ها:
نویسندگان
F Mansouri
Ceramic Department, Materials and Energy Research Center, Tehran, Iran
Z. Khakpour
Ceramic Department, Materials and Energy Research Center, Tehran, Iran
A. Maghsoudipour
Ceramic Department, Materials and Energy Research Center, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :