Investigation on Mechanical and Electrical Properties of Cu-Ti Nanocomposite Produced by Mechanical Alloying
محل انتشار: ماهنامه بین المللی مهندسی، دوره: 33، شماره: 9
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 291
فایل این مقاله در 7 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJE-33-9_009
تاریخ نمایه سازی: 6 اردیبهشت 1400
چکیده مقاله:
In this paper, Cu-Ti nanocomposite synthesized via ball milling of copper-titanium powders in ۱, ۳, and ۶ of weight percentage compounds. The vial speed was ۳۵۰ rpm and ball to powder weight ratio kept at ۱۵:۱ under Argon atmosphere, and the time of milling was ۹۰ h. Obtained powders were studied by scanning electron microscopy (SEM), X-ray diffraction (XRD), and dynamic light scattering (DLS). Crystallite size, lattice strain, and lattice constant were calculated by Rietveld refinement with Maud software. The results show a decrease in the crystallite size, and an increase in the internal strain and lattice parameter. Furthermore, the lattice parameter grew by increasing the percentage of titanium. Then, the powders compressed by the cold press and annealed at ۶۵۰˚C, and finally, their micro-hardness and electrical resistance were measured. These analyses show that via increasing the proportion of titanium, Cu-۶wt%Ti with ۳۱۲ Vickers had the highest micro-hardness; due to the increasing the work hardening. Moreover, the results of the electrical resistance illustrate through increasing the amount of alloying material, the electrical resistance grew which the highest electrical conductivity was Cu-۱wt%Ti with ۰.۳۶ Ω.
کلیدواژه ها:
نویسندگان
R. M. Babaheydari
Department of Material Science and Engineering, Shahid Bahonar University of Kerman, Iran
S. O. Mirabootalebi
Department of Material Science and Engineering, Shahid Bahonar University of Kerman, Iran
G. H. Akbari
Department of Material Science and Engineering, Shahid Bahonar University of Kerman, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :