Numerical and Experimental Investigation of Thickness Variation in the Spinning Process of Al-1060 Alloy
سال انتشار: 1395
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 270
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_MPMPJ-5-4_001
تاریخ نمایه سازی: 7 بهمن 1399
چکیده مقاله:
Metal spinning as a kind of manufacturing process has capability to shape hollow components. In present work shear spinning process is used to formplates into conical shapes. Moreover, the aim of this research is to demonstrate the impact of the process parameters (i.e. feeding rate and spindle speed) on wall thickness. This approachwas done by experimental and finite elements method. The results illustrated that wall thickness decreases while feeding rate increases in spinning process. The experimental results confirm the Finite element analysis (FEA) results during thickness evaluations so this shows that FEA results are reliable for this specific case. The results of analysis reveals that the best condition for spinning is for feeding rate of 40 mm/min and spindle speed of 50 rpm in which highest thickness of 1mm is obtained. In consequence, the findings also illustrated that by decreasing the feeding rate and spindle speed, higher thickeners can be observed during shear spinning process.
کلیدواژه ها:
نویسندگان
Mohammad Honarpisheh
Faculty of Mechanical Engineering, University of Kashan, Kashan, Iran
Shayan Namazikhah
Faculty of Engineering, Jasb branch, Islamic Azad University
Iman Alinaghian
Faculty of Mechanical Engineering, University of Kashan, Kashan, Iran