Effect of Rhenium on Ag/ SrTiO۳ Catalyst in Ethylene Epoxidation Reaction: Synthesize, Characterization and Evaluation
محل انتشار: مجله پردازش گاز، دوره: 8، شماره: 2
سال انتشار: 1399
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 294
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_GPJU-8-2_002
تاریخ نمایه سازی: 6 دی 1399
چکیده مقاله:
In this study, silver catalysts on SrTiO۳ support contain cesium, and rhenium promoters are synthesized using the impregnation method for ethylene epoxidation reaction. SEM results show a small decrease in metal dispersion by adding cesium (۳ catalyst. Rhenium leads to the weakening of the peaks intensity in the crystalline structure of the catalysts. In addition, the predominance of Ag (۱۱۱) surface facets compared to the Ag (۱۱۰) and Ag (۱۰۰) surface facets are obvious in the XRD results. The ability of the catalysts in oxygen adsorption and desorption is studied through O۲-TPD results. Ethylene conversion increases by adding rhenium to the Ag-Cs/SrTiO۳ catalyst in the temperature range of ۲۱۰ to ۲۲۰ °C. Ethylene oxide selectivity increases slightly from ۸۰% to ۸۴% in the Ag-Cs-Re/SrTiO۳ while this value in the Ag-Cs/SrTiO۳ catalyst decreases from ۶۵% to ۳۴%, in the mentioned temperature range. Severe sensitivity of the rhenium-conation catalyst to the inlet concentration of carbon dioxide (۶ mol %) is observed through a ۵۰% drop in the produced ethylene oxide compared to the product which doesn’t have any carbon dioxide in the feed.
کلیدواژه ها:
نویسندگان
Shiva Darake
Department of Chemical Engineering, Faculty of Engineering, University of Kashan, Kashan, Iran / Research and Development Group, Exir Novin Farayand Asia Company, Tehran ۱۳۸۹۷۱۴۳۶۱, Iran
Reza Golhosseini
Department of Chemical Engineering, Faculty of Engineering, University of Kashan, Kashan, Iran
Alireza Mohammadrezaei
Research and Development Group, Exir Novin Farayand Asia Company, Tehran ۱۳۸۹۷۱۴۳۶۱, Iran
Morteza Asghari
Department of Chemical Engineering, Faculty of Engineering, University of Kashan, Kashan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :