Synthesis and structure evaluation of MoSi2 – Mo5Si3 composite
محل انتشار: دومین کنفرانس بین المللی کامپوزیت
سال انتشار: 1389
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,126
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
COMPOSIT02_206
تاریخ نمایه سازی: 24 مهر 1389
چکیده مقاله:
In order to synthesize MoSi2 – Mo5Si3 composites, pure molybdenum and silicone powders were milled with employing an attritor mill for 20 hr. Mechanically alloyed (MAed) powders were annealed in an atmosphere controlled furnace for 3, 5 and 7 hr at 1100˚C. Metallurgical characteristics of MAed and annealed powders were evaluated by scanning electron microscopy (SEM) and X-ray diffraction technique (XRD) and the obtained results were compared for all prepared samples. The results did not confirm the presence of any related intermetallics after MA. However, MoSi2 and Mo5Si3 were successfully formed during annealing at 1100˚C. The further annealing caused the enhancement of the volume fraction of MoSi2, while that of Mo5Si3 was decreased, as during annealing for 7 hr the volume fraction of Mo5Si3 was negligible.
کلیدواژه ها:
نویسندگان
M Erfanmanesh
Master of science student
S.R Bakhshi
Assistant professor, Department of Materials Engineering
M Salekbafghi
Master of science student
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :