The investigation on the role of nano sized calcium carbonate particles in a MDPE on its resistant against perforation
محل انتشار: دومین کنفرانس بین المللی کامپوزیت
سال انتشار: 1389
نوع سند: مقاله کنفرانسی
زبان: انگلیسی
مشاهده: 1,421
فایل این مقاله در 6 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
COMPOSIT02_165
تاریخ نمایه سازی: 24 مهر 1389
چکیده مقاله:
In this article, the role of nano size calcium carbonate on resistant against penetration and perforation of MDPE was investigated through experiments. The results of perforation tests showed that the tearing behaviour of MDPE/CaCO3 nanocomposites depends on their relative amount of CaCO3 particles. Addition of CaCO3 nanoparticles to pure PE increased both the applied force for the first penetration of the indenter in the sample and the peak force (perforation force). In addition, this nanocomposite sample consumed the greatest energy for the whole perforation test. The plastic zone regions around the perforated area were inspected using scanning electron microscopy. The toughening mechanisms of shear yielding and massive shear yielding observed. The mechanical response of composite samples containing CaCO3 nanoparticles greater than 5 wt.% in a perforation test was found to be different. Fracture surface images showed when calcium carbonate content is higher than 5 weight percent, agglomeration of nano particles occured. Debonding stress relates on particle size inversely and debonding stress will be raised as particle size decreases. Therefore, as shown in the SEM micrograph of a nanocomposite sample with 10 wt.% CaCO3 nanoparticles, the crack has been nucleated and then propagated during different stages of the test.
کلیدواژه ها:
نویسندگان
F Hosseinabadi
Graduate student
S.M Zebarjad
Associated Professor
M Mazinani
Assistant Professor
N Modghan
Graduate student,Department of Materials Science and Engineering Ferdowsi University Of Mashhad, Mashhad,Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :