Improving Mechanical Properties of Nanocomposite-based Epoxy by High-impact Polystyrene and Multiwalled Carbon Nanotubes: Optimizing by a Mixture Design Approach
سال انتشار: 1396
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 343
فایل این مقاله در 13 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_MACS-4-1_004
تاریخ نمایه سازی: 14 تیر 1399
چکیده مقاله:
In the current study the influence of weight percentage of HIPS, weight percentage of CNT and hardener content on damping 1st and damping 2nd properties of epoxy/HIPS/CNT hybrid composite wase valuated. Mixture design methodology was employed to generate mathematical models for predicting damping 1st and damping 2nd behaviors of new mentioned hybrid nanocomposite as function of physical factors and optimizing desired mechanical properties. The maximum and minimum values of damping 1st occurred in run numbers 7 and 1 and were 3.71%and 1.64 % respectively, moreover maximum and minimum values of damping 2nd occurred in coded levels 9 and 1 with the values of 4.25% and 1.82 % respectively. Results of analysis of variance showed that input variables had linear effect on both of the studied responses, also two component interactions X1*X2, X1*X3 and X2*X3 affected damping 1st and damping 2nd due to their obtained P-values. Optimization results described that the highest value for damping 1st and damping 2nd were 3.53% and 4.11% respectively.Coded values were HIPS= 0.222, CNT= 0.301 and hardener= 0.476 and corresponding mixture components were HIPS=4.18wt%, CNT= 1.12 wt% and hardener= 25.75phr respectively.
کلیدواژه ها:
نویسندگان
Yasser Rostamiyan
Department of Mechanical Engineering, Sari Branch, Islamic Azad University, Sari, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :