Flexural Behavior of Fiber–Metal Laminates Reinforced with Surface-Functionalized Nanoclay
سال انتشار: 1397
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 310
فایل این مقاله در 8 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_MACS-5-2_005
تاریخ نمایه سازی: 14 تیر 1399
چکیده مقاله:
The effects of surface-functionalized Na+-montmorillonite nanoclay particles on the flexural behavior of E-glass fiber-reinforced aluminum (GLARE) laminates were investigated. The nanoclay particles were subjected to surface functionalization using 3-(trimethoxysilyl)propylamine to increase their compatibility with the epoxy matrix and improve their dispersion within the matrix. Experimental results indicated that the GLARE laminates achieved the highest flexural strength (61%) and energy absorption (51%) at an addition of 3 wt% functionalized nanoclay. The highest flexural modulus (67% increase) was observed at an addition of 5 wt% functionalized nanoclay. The flexural properties of the functionalized nanoclay-filled GLARE laminates were significantly better than those of untreated nanoclay-filled GLARE laminates. Microscopic observations suggested that the introduction of functionalized nanoclay particles markedly enhanced the interfacial adhesion between the matrix and the E-glass fibers.
کلیدواژه ها:
نویسندگان
Sh. Vahedi
Materials Science and Engineering Faculty, K.N. Toosi University of Technology, Tehran, Iran
S.M.H. Siadati
Materials Science and Engineering Faculty, K.N. Toosi University of Technology, Tehran, Iran
H. Khosravi
Department of Materials Engineering, Faculty of Engineering, University of Sistan and Baluchestan, Zahedan, Iran
A. Shahrabi
Materials Science and Engineering Faculty, K.N. Toosi University of Technology, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :