Sintered Steel Composites Reinforced with Ceramic Nanoparticles: Fabrication, Characteristics and Wear Behavior
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 266
فایل این مقاله در 10 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_MACS-6-2_012
تاریخ نمایه سازی: 14 تیر 1399
چکیده مقاله:
Steel composites reinforced with alumina nanoparticles were prepared by powder metallurgy process. Samples containing two different amounts of carbon (0.35 and 0.55 wt.%) and 0-5 wt.% Al2O3 nanoparticles were fabricated by mixing, compacting and sintering of diffusion bonded Distaloy AE powder. The density, hardness and wear tests were performed on the prepared samples. Furthermore, the microstructures and worn surfaces were analyzed by optical and scanning electron microscope (SEM), respectively. The wear tests were carried out in forces of 30, 40 and 50 kN and 1000 m distance in dry condition and ambient temperature. The results showed that increasing the alumina nanoparticles would reduce the density (~ 10.8 and 9.6 % for 0.35 and 0.55 wt.% C, respectively) and would increase the hardness (~ 14.1 and 7.2 % for 0.35 and 0.55 wt.% C, respectively) of sintered samples. With increasing carbon content, the amount of lost material and the rate of wear decrease. The lost volume increases with increasing wear distance and applied force. Addition of reinforcement to the steel matrix, improves the wear resistance up to 3 wt.% alumina nanoparticles. This increase in the samples varies between 30% to 73%. More increasing of alumina (5 wt.%) decreases the wear resistant of samples. The wear mechanisms including oxidation in low forces that convert to adhesive and abrasive with increasing applied force. The wear curves indicate that as the wear distance increases, the lost volume increases, while the wear rate decreases.
کلیدواژه ها:
نویسندگان
Hassan Abdoos
Department of Nano Technology, Nano-Materials Division, Faculty of New Science and Technology, Semnan University, Semnan, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :