Chemical Modification of Lignite and Investigation of its Properties in Controlling Fluid Loss of Oil Well Cement Slurries
سال انتشار: 1398
نوع سند: مقاله ژورنالی
زبان: انگلیسی
مشاهده: 306
فایل این مقاله در 15 صفحه با فرمت PDF قابل دریافت می باشد
- صدور گواهی نمایه سازی
- من نویسنده این مقاله هستم
استخراج به نرم افزارهای پژوهشی:
شناسه ملی سند علمی:
JR_IJOGST-8-4_003
تاریخ نمایه سازی: 6 خرداد 1399
چکیده مقاله:
The aim of this research was to produce a convenient additive for enhancing the properties, especially the fluid loss, of oil well cement slurries. In this regard, a variety of drilling/cementing chemical additives known as fluid loss controllers were prepared through derivatization and chemical modification of lignite. Lignite-based graft copolymers were synthesized using different groups of acrylic monomers via aqueous the free radical polymerization method. Then, it was allowed to react with sulfomethylating agents to enhance its water solubility. Subsequently, a comparative sulfomethylated lignite was prepared and employed as the backbone in the free radical polymerization. ATR-FTIR and elemental analyses were performed to demonstrate the structures of the fluid loss controller and incorporated elements. The performance of these additives in improving the properties of oil well cement slurries was investigated through analyzing the quality of fluid loss controller in saline saturated slurries. Under similar desired well conditions, i.e. a compressive strength of 800-1100 psi, a thickening time of 400 minutes, and a viscosity of 25 cP, a fluid loss below 130 ml API was obtained. The best standard performance was assigned to the cement slurry which employed sulfomethylated lignite graft copolymer.
کلیدواژه ها:
نویسندگان
Ali Nemati Kharat
Professor, School of Chemistry, University College of Science, University of Tehran, Tehran, Iran
Ali akbar Ghaffari
M.S. Student, School of Chemistry, University College of Science, University of Tehran, Tehran, Iran
مراجع و منابع این مقاله:
لیست زیر مراجع و منابع استفاده شده در این مقاله را نمایش می دهد. این مراجع به صورت کاملا ماشینی و بر اساس هوش مصنوعی استخراج شده اند و لذا ممکن است دارای اشکالاتی باشند که به مرور زمان دقت استخراج این محتوا افزایش می یابد. مراجعی که مقالات مربوط به آنها در سیویلیکا نمایه شده و پیدا شده اند، به خود مقاله لینک شده اند :