Effect of Ball to Powder Weight Ratio on the Particle Size of WC-10%Co Nanocomposite
- سال انتشار: 1386
- محل انتشار: دومین کنفرانس نانوساختارها
- کد COI اختصاصی: CNS02_093
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1856
نویسندگان
Islamic Azad University-Saveh Centre, Saveh
Islamic Azad University-Saveh Centre, Saveh
bMaham Research Centre,
Maham Research Centre
چکیده
Ultrafine WC and Co powders were milled by high energy ball milling with different ball to powder ratios (5, 15, 25 and 35) to produce nanoparticles of WC-10Co composite. The particle size was measured by electron microscopy (SEM and TEM). The particle size analyses by TEM were in an appropriate agreement with the SEM results. The particle size was found less than 100 nm from 15 ball to powder ratio.کلیدواژه ها
Nanoparticle; WC-10Co; High energy ball milling; Ball to powder ratio; Electron microscopyمقالات مرتبط جدید
- بررسی عوامل مژثر بر پیشگیری و مدیریت پدیده خودسوزی زغال سنگ در صنعت معدن کاری زیرزمینی
- پیش بینی لرزش زمین با روش های شبکه عصبی مصنوعی و رگرسیون چندمتغیره (مطالعه موردی: معدن سنگ آهن شماره یک گل گهر)
- ارزیابی درجه آلودگی فلزات سنگین با استفاده از شاخص آماری ضریب غنی شدگی در رسوبات منطقه وبژه اقتصادی بندر شهیدر جائی
- تعیین مناسب ترین روش آب گیری از باطله های کارخانه تغلیظ ۳ مجتمع مس سرچشمه
- کاربرد روش تحلیل سلسله مراتبی AHP در مهندسی معدن
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.