Improvements to the sintering behavior of yttria-stabilized zirconia coating by addition of Aluminum
- سال انتشار: 1395
- محل انتشار: چهارمین کنفرانس بین المللی آلومینیوم ایران IIAC۲۰۱۶
- کد COI اختصاصی: IIAC04_071
- زبان مقاله: انگلیسی
- تعداد مشاهده: 372
نویسندگان
Department of Materials Engineering, University of Tabriz, Tabriz, P.O. Box: ۵۱۶۶۶۱۶۴۷۱, Iran
Department of Materials Engineering, University of Tabriz, Tabriz, P.O. Box: ۵۱۶۶۶۱۶۴۷۱, Iran
چکیده
Yttria-stabilized zirconia (YSZ) is the most widely used material in thermal barrier coatings. The main difficulty in fabricating ceramic coatings on metal substrates using the electrophoretic deposition process (EPD) is problems caused by the volume shrinkage during the sintering of the green form ceramic coating. In this research, a combination of EPD and reaction bonding processes has been used for fabrication of an adherent and crack-free coating on Iron-Nickel superalloy. Aluminum particles were added to the suspension of YSZ in acetone. By using EPD of aluminum and YSZ particles, a uniform green coating formed on the substrate by applying voltage of 6 V during 3 min. After oxidation of aluminum at 660°C for 2 h and sintering at 1100°C for 2 h, an adherent and crack-free coating was obtained. Addition of aluminum to the green coating not only has reduced the sintering temperature of the YSZ coating about 200°C, but also has compensated the shrinkage of the coating by the volume expansion due to the oxidation of aluminum.کلیدواژه ها
Aluminum, Yttria-stabilized Zirconia, Electrophoretic deposition, Reaction bonding, Coatingمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.