LOW TEMPERATURE MOLTEN SALT SYNTHESS OF NANOCRYSTALLINE MGALO, SPINEL POWDER USING NACL SALT MEDIA
- سال انتشار: 1390
- محل انتشار: سومین کنفرانس بین المللی مواد فوق ریزدانه و نانوساختار
- کد COI اختصاصی: UFGNSM03_069
- زبان مقاله: انگلیسی
- تعداد مشاهده: 357
نویسندگان
School of Metallurgy and Materials Engineering, Iran University of Science and Technology Tehran, Iran
School of Metallurgy and Materials Engineering, Iran University of Science and Technology Tehran, Iran
School of Metallurgy and Materials Engineering, Iran University of Science and Technology Tehran, Iran
چکیده
MgAl2O4 (MA) spinel nano powder was synthesized using a molten salt technique, by heating stochiometric composition of MgO and AlOOH. NaCl salt was used as reactor media for MA spinel formation. Reactants and molten salt mixtures were fired in an alumina crucible for 3 h at temperature ranges from 850 °C to 1000 °C. The synthesis temperature was decreased from 1300 C required by the conventional solid-solid reaction process to 850 C for molten salt approach. The synthesized powders were characterized by X-ray diffraction pattern OXRD), scaning electron microscopy (SEM) and Brunauer-Emmett–Teller technique (BET). XRD revealed complete formation of MA without remaining of any secondary phase for synthesized powder fired at 850 °C for 3 h. Moreover, electron microscopy illustrated that the MA morphology and size was the same as the nano boehmite morphology which confirmed the existence of a template process mechanism during the molten salt synthesis. In addition, high surface area for nano MA powders was achieved in this method.کلیدواژه ها
Molten salt; nanopowder, synthesis; low temperature, MgAl2O4مقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.