Effect of Post-Warm Caliber Rolling (WCR) on ECAPed CP-Ti Grade2 Parts
- سال انتشار: 1395
- محل انتشار: سیزدهمین کنفرانس مهندسی ساخت و تولید ایران
- کد COI اختصاصی: ICME013_073
- زبان مقاله: انگلیسی
- تعداد مشاهده: 507
نویسندگان
University of Tehran, Master of Science Student
University of Tehran, Assistant Professor
چکیده
Nowadays needs to materials with good strength and ductility simultaneously have become a drastic challenge. Also CP-Ti is an applicable material particularly for Aerospace and Bio fields. As-received CP-Ti represents relatively poor quality in terms of strength which can be addressed successfully by applying Equal Channel Angular Pressing (ECAP). The most important shortcoming is that the ECAP results in a slump in the ductility, hence the following forming processes encounter serious limitation in form of formability. In order to increase ductility and formability of the stated material, Warm Caliber Rolling (WCR) used after ECAP. As extracted by results from this study, specimens which underwent WCR show the uniform plastic deformation during passes. Also escalating workability of them is another advantage of post-WCR processکلیدواژه ها
Strength, Ductility, ECAP, Warm Caliber Rolling, Formabilityمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.