Solid-state synthesis of LiFePO4/C cathode material for application in Li-ion batteries
- سال انتشار: 1395
- محل انتشار: دومین کنفرانس بین المللی یافته های نوین پژوهشی در شیمی و مهندسی شیمی
- کد COI اختصاصی: CHCONF02_552
- زبان مقاله: انگلیسی
- تعداد مشاهده: 739
نویسندگان
Department of chemistry, Amirkabir University of Technology, Tehran, Iran
Department of chemistry, Amirkabir University of Technology, Tehran, Iran
Department of chemistry, Amirkabir University of Technology, Tehran, Iran
چکیده
The LiFePO4/C prepared using FeC2O4.2H2O, LiOH.H2O, NH4H2PO4 and tartaric acid via solid-state reaction. Charge-discharge and electrochemical impedance spectroscopy (EIS) tests were applied to investigate electrochemical performance of the LiFePO4/C sample synthesized. The synthesis condition of LiFePO4/C was ball-milling with speed of 250 rpm. This sample had a discharge capacity of 135 mAh.g-1 at 0.1C.کلیدواژه ها
lithium-ion batteries, cathode materials, LiFePO4/C, solid-state, ball-millingمقالات مرتبط جدید
- ؛ GRP-۷۸ سنتز و بهینه سازی نانوکامپوزیت آهن نیکل جهت تخلیض ایمونوگلوبولین
- نانوکامپوزیت مبتنی بر کربوکسی متیل سلولز: یک ماده زیستی امیدوار کننده برای کاربردهای زیست پزشکی
- Multi component Reaction of Isoquinoline, Dialkyl acetylenedicarboxylate, Aldehydes and Dimedone Catalyzed by Bio-CuO-NPs
- Synthesize of forward osmosis membrane with Zinc Oxide interlayer for enhanced water desalination
- Co-doping effects in CdWO۴ scintillator thin film as alpha counters: Ag and Gd case
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.