Feasibility of Joining Al-20%Mg2Si In-Situ Composite By TIG Welding
- سال انتشار: 1391
- محل انتشار: دومین کنفرانس بین المللی آلومینیوم
- کد COI اختصاصی: IIAC02_089
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1272
نویسندگان
Department of Manufacturing Engineering, FKM, Universiti Teknologi Malaysia, Johor, ۸۱۳۱۰, Malaysia
Department of Manufacturing Engineering, FKM, Universiti Teknologi Malaysia, Johor, ۸۱۳۱۰, Malaysia Department of Materials Engineering, FKM, Universiti Teknologi Malaysia, Johor, ۸۱۳۱۰, Malaysia
Department of Materials Engineering, FKM, Universiti Teknologi Malaysia, Johor, ۸۱۳۱۰, Malaysia
چکیده
The feasibility of joining an in situ Al-20%Mg2Si composite by TIG is investigated. Welding current was varied at five different values between 80 and 100 amp. Different areas were identified in the weldment region due to effect of welding specification. Mechanical properties of joints were evaluated by Tensile and microhardness tests. Joints welded with a welding current in the range of 80-85 amp displayed the highest degree of hardness. The fracture produced in the welded specimens was in the base metal MMC, indicating a strong interface between the base MMC and the weld. Therefore, the study finds that in situ Al-Mg2Si MMC can in fact be welded using TIG and Al-Si filler metal.کلیدواژه ها
Aluminium; In-situ composite; Joining; TIGمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.