Effect of Annealing on Microstructure and Microhardness of Melt-Spun Al–20Si–5Fe Ribbons
- سال انتشار: 1391
- محل انتشار: دومین کنفرانس بین المللی آلومینیوم
- کد COI اختصاصی: IIAC02_022
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1361
نویسندگان
Department of Materials Science and Technology, Sharif University of Technology, Tehran, P.O. Box: ۱۱۱۵۵-۹۴۶۶, Iran
Department of Materials Science and Technology, Sharif University of Technology, Tehran, P.O. Box: ۱۱۱۵۵-۹۴۶۶, Iran
چکیده
Rapid solidification process provides a typical case of non-equilibrium solidification, hence refines significantly the microstructural features (grain size and size of second phase/intermetallic particles), reduces segregation effects, increases the solid solubility extension and induces constitutional changes in alloys (formation of supersaturated solid solutions, metastable crystalline intermediate, and amorphous phases). The present study is concerned with the effect of annealing on microstructure and microhardness of rapidly solidified ternary Al–20Si–5Fe alloy at cooling rates between 106 and 107 K/s using the melt spinning technique. The melt spun ribbons characterized using X-ray diffractometry and scanning electron microscopy. The obtained results demonstrated the size of primary silicon, the intermetallic phases, and the eutectic silicon in the melt-spun ribbons were extremely modified as compared with those found in conventionally processed materials. Annealing at various temperatures from 200 to 450○C for a specific time disclosed that the two predetermined zones can’t be distinguished after heat treatment. Also, increasing of the temperature reduced the microhardness. Furthermore, the solid solubility levels of alloying elements (Si and Fe) in Al substantially increased which resulted in solid solution strengthening.کلیدواژه ها
Al-20Si-5Fe alloy; Rapid solidification Process; Melt-Spinning; Microstructure; Microhardness; Annealingمقالات مرتبط جدید
- مطالعه تجربی و مقایسه رفتار مکانیکی گلار۱/۲ و گلار ۲/۳ تحت بار خمشی
- Investigation effect of process parameters of Al۶۰۶۱ composites fabricated by FSP on microstructure, mechanical properties with minitab and designexpert
- بررسی خواص جوشمان های سطحی دو لایه بر روی ورق فولادی دو لایه
- مکانیزم ها در دیگ های بخار
- Numerical Study on the cavitation patterns in a Francis turbine
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.