The effect of substrate's heat treatment on microstructure and mechanical properties TLP bonding X-45 and FSX-414 cobalt based superalloys
- سال انتشار: 1399
- محل انتشار: سومین کنفرانس بین المللی جوشکاری و آزمایش های غیرمخرب ایران، بیست و یکمین کنفرانس ملی جوش و بازرسی و دهمین کنفرانس ملی آزمایش های غیرمخرب
- کد COI اختصاصی: INCWI21_012
- زبان مقاله: انگلیسی
- تعداد مشاهده: 280
نویسندگان
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
Department of Materials Engineering, Isfahan University of Technology, Isfahan, Iran
Department of Materials Engineering, Faculty of Engineering, Razi University, Kermanshah, Iran.
Advanced Materials Research Center, Department of Materials Engineering, Najafabad Branch, Islamic Azad University, Najafabad, Iran
چکیده
In this study, a dissimilar joint of cobalt based superalloys X-45 and FSX-414 has been created under the standard heat treatment conditions with the nickel-based BNi-9interlayer with the thickness of 50μm by the transient liquid phase bonding process. Solution heat treatment (1150°C/4h) was used for bonding and the aging heat treatment(980°C/4h) for the homogenization of the bond. Optical metallography, Field Emission Scanning Electron Microscope with Energy Dispersive X-ray Spectroscopy, Differentialscanning calorimetry, micro-hardness test and shear strength test were used for the characterization of microstructural and mechanical evolution in base metals and bonds.The solution heat treatment leads to the dissolution of a part of the M23C6 and M6C carbides in the substrate of superalloys, which due to the aging heat treatment secondaryand fine carbides M23C6 precipitate in the substrate and help strengthen the superalloys. The diffusion of the boron from the molten interlayer to the base metals resulted in the complete isothermal solidification and a nickel-based single-phase solid solution has been developed. Cobalt-chromium-tungsten-molybdenum-based carboboridesprecipitation with high hardness in the vicinity of the isothermal solidification zone and in base metals results in the non-homogeneity of microhardness profile along the bonding area. Homogenization heat treatment did not have an effect on the omission of these precipitations, but by more uniform redistribution of the alloying elements strengthen solid solution that could increase shear strength from 655 to 688 MPa, which is somewhat equivalent to the shear strength of the 45-X alloy and also 93% of the shear strength of the FSX-414 alloy.کلیدواژه ها
Transient liquid phase; Cobalt-based superalloy, fist nozzle-stageمقالات مرتبط جدید
- مدلسازی ترمودینامیک و امکان سنجی بازیافت انرژی حرارتی از دودکش هیتر ایستگاههای اصلی گاز(CGS) با استفاده از تکنولوژی ترموالکتریک
- مقایسه بهینه سازی ضریب انتقال حرارتی در ساختمان ها به کمک الگوریتم فاخته و الگوریتم ژنتیک
- ساخت سیستم فتوولتائیک ساختمانی با استفاده از دنبال کننده نور طبیعی در روز و نور مصنوعی در شب
- بهره برداری از شبکه های برق در حضور هاب انرژی
- دیپلماسی انرژی ایران در حوزه منطقه ای: (۲۰۰۳-۲۰۲۳)
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.