Optimization of magnetic components used in storing radar information

  • سال انتشار: 1398
  • محل انتشار: پنجمین همایش بین المللی علوم و تکنولوژی با رویکرد توسعه پایدار
  • کد COI اختصاصی: TECHSD05_019
  • زبان مقاله: انگلیسی
  • تعداد مشاهده: 436
دانلود فایل این مقاله

نویسندگان

m shahriari

Phd student in malekashtar university

a ghasemi

supervisor ,malekashtar in shahinshahr Esfahan university

m tavusi

advisor, shahinshahr Esfahan university

t sodaee

advisor, phd student in malekashtar university

چکیده

Mechanical alloying of the FeCo equiatomic-magnetic alloy from elemental powders has been studied. The as-milled powders were characterized using scanning electron microscopy (SEM), x-ray diffraction (XRD) and vibrating sample magnetometry (VSM). ?Fe1−x??Cox?(X = 0.2, 0.25, 0.3, 0.35, 0.4 ,0.45 and 0.5) powders were prepared by mechanical alloying after 15,20,25 and 30 hours. magnetic properties were investigated based on microstructure.The saturation magnetization of the mixtures of Fe and Co increases with milling time, indicating an increasing homogeneity in composition and the phase formation. It is found that the saturation magnetization is also dependent on the Co content, which reaches the highest value of 266 emu/g at Fe60Co40.

کلیدواژه ها

mechanical alloying, FeCo, magnetic properties, application

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.