Microstructure Evolution and Mechanical Properties of Friction Stir Welded Dissimilar Joints of AA5083 and AA1050 Aluminum Alloys

سال انتشار: 1397
محل انتشار: پنجمین کنفرانس بین المللی آلومینیوم ایران
کد COI اختصاصی: IIAC05_051
زبان مقاله: انگلیسی
تعداد مشاهده: 458

نویسندگان

School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Tehran, Iran

Department of Materials Science and Engineering, Faculty of Engineering, Shahid Chamran University of Ahvaz, Ahvaz, Iran

M.R Aboutalebi

School of Metallurgy and Materials Engineering, Iran University of Science and Technology (IUST), Tehran, Iran

چکیده

In the present work, the friction stir processing was applied to join the dissimilar structural alloys of AA5083 and AA1050. The microstructure evolution during friction stir welding of alloys were investigated by means of the optical microscope (OM), field emission scanning electron microscopy (FESEM) equipped with energy dispersive spectroscopy (EDS). The mechanical properties of the dissimilar FSW joint were evaluated using hardness and tensile tests. Experimental results showed that the nugget zone (NZ) exhibited equiaxed recrystallized grains of the two materials with flowing shape and mainly composed of the advancing side (AS) material. The ultimate tensile and yield strengths of the dissimilar FSW joint was higher than the AA1050 base metal while lower than the AA5083, having fractured on the AA1050 side

کلیدواژه ها

Aluminum alloys; Dissimilar friction stir welding; Microstructure; Mechanical properties.

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.