Solution Combustion Synthesis of Cobalt Oxide Nanostructure as a Supercapacitor
- سال انتشار: 1397
- محل انتشار: شانزدهمین کنگره ملی مهندسی شیمی ایران
- کد COI اختصاصی: NICEC16_711
- زبان مقاله: انگلیسی
- تعداد مشاهده: 326
نویسندگان
Department of Chemical Engineering, Amirkabir University Of Technology, Tehran, Iran
Department of Chemical Engineering, Amirkabir University Of Technology, Tehran, Iran
چکیده
Cobalt oxide nanoparticles (Co3O4) have been prepared by the solution combustion synthesis from cobalt nitrate as the oxidizer and urea as the fuel at the stochiometric fuel-to-oxidant ratio. X-ray powder diffraction (XRD) was demonstrated the crystalline nanostructure of the cobalt oxide by the size of . The Brunauer-Emmett-Teller (BET) specific surface area was meassured by 54.69 m2.g-1. Electrochemical characterization of the synthesized powders, i.e., cyclic voltametry, was conducted in 6 M KOH as the electrolyte where a gravimetric capacitance of 264.16 F.g-1 was obtained. Furthermore, the synthesized cobalt oxide showed the surface area of 54.69 m2.g-1 together with a capacitive behavior. Therefore, such Co3O4 synthesized by the solution combustion synthesis could be an appropriate candidate as the electrochemical capacitor.کلیدواژه ها
Cobalt oxide, Nanoparticle, Electrochemical capacitor, Solution combustionمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.