comparison of the surface pretreatment of mild steel by acid and alkaline solutions for corrosion enhancement of silane coatings
- سال انتشار: 1397
- محل انتشار: هفتمین کنفرانس بین المللی مهندسی مواد و متالورژی و دوازدهمین همایش ملی مشترک انجمن مهندسی متالورژی و مواد ایران و انجمن ریخته گری ایران
- کد COI اختصاصی: IMES12_320
- زبان مقاله: انگلیسی
- تعداد مشاهده: 662
نویسندگان
MSc Student, School of Metallurgy and Materials Engineering, Faculty of Engineering, University of Tehran, Tehran, Iran
Full professor, School of Metallurgy and Materials Engineering, Faculty of Engineering, University of Tehran, Tehran, Iran
Full professor, School of Chemistry, College of Science, University of Tehran, Tehran, Iran
MSc Student, School of Metallurgy and Materials Engineering, Faculty of Engineering, University of Tehran, Tehran, Iran
چکیده
In this work, the effect of acidic and basic treatments on mild steel samples before applying silane coatings was investigated. H2SO4 and H3PO4 as acid solutions with pH and 25 g/L (pH 13.25) NaOH as the basic solution were used. Coated samples were prepared using (3-Glycidyloxypropyl) trimethoxysilane and tetraethylorthosilicate, as silane precursors through dip coating method. Scanning electron microscopy (SEM) and potentiodynamic polarization tests were applied for investigating the corrosion behavior of mild steels in treatment media. Electrochemical impedance spectroscopy (EIS) was carried out for evaluating the corrosion performance of silane coated steels at different immersion times in 0.1 NaCl. SEM images showed good distribution and different morphology of corrosion products on H3PO4 treated mild steel. Polarization curves also showed the higher tendency to corrosion of mild steels in acidic solutions than the basic one. EIS results for silane coated steel showed the best corrosion behavior for samples treated with H3PO4 solution. This could be related to better adhesion of the active silanols in the sol to surface hydroxides of the H3PO4 treated steel which is converted to strong covalent bonds during curing. Visual appearance of the samples also confirmed these findings.کلیدواژه ها
Mild Steel, Corrosion performance, Silane coating, Acidic treatment, Basic treatment, Electrochemical impedance spectroscopyمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.