Effect of thermomechanical processing on mechanical properties of FeMnCoCr high entropy alloy
- سال انتشار: 1397
- محل انتشار: هفتمین کنفرانس بین المللی مهندسی مواد و متالورژی و دوازدهمین همایش ملی مشترک انجمن مهندسی متالورژی و مواد ایران و انجمن ریخته گری ایران
- کد COI اختصاصی: IMES12_188
- زبان مقاله: انگلیسی
- تعداد مشاهده: 359
نویسندگان
Master student of Metal forming, School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
Full Professor, School of Metallurgy and Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
چکیده
In the current study, two distinct microstructures with different grain size and dislocation distribution wereobtained through rolling to total reduction of 60% at temperatures of 800 and 1000 ℃. The results indicatethat the deformed matrix was maintained at 800 and this leads to banded-like accumulation ofdislocations. Therefore the initial microstructure provides many potential nucleation sites for HCP εformation. This was justified considering the higher values of room temperature strength and ductility forthe material rolled at 800 ℃. In contrast, in the material rolled at 1000 the uniform and nearly equiaxeddislocation distribution were obtained which was ascribed to multiple slip occurred within recrystallizedgrains. This can leads to long distances regions within the grains which was free of geometrically necessarydislocations. Therefore, there are long orientation gradients regions which HCP formation was stopped orpostponed during tensile loading at room temperature.کلیدواژه ها
high entropy alloys, geometrically necessary dislocations, mechanical properties, transformation induced plasticityمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.