Surveying the Adhesive Interaction on the Laminated Particleboard
- سال انتشار: 1397
- محل انتشار: بیست و یکمین کنفرانس شیمی فیزیک انجمن شیمی ایران
- کد COI اختصاصی: ISPTC21_260
- زبان مقاله: انگلیسی
- تعداد مشاهده: 331
نویسندگان
Department of Chemistry, Imam Mohammad Bagher University, P.O. Box ۴۸۱۶۸-۳۱۱۶۷ Sari, Iran
چکیده
Adhesives are used in many different applications with wood products same asparticleboard (PB). In this work, the curing reaction of system consisting of some adhesive sameas urea formaldehyde (UF), urea-melamine formaldehyde (MUF) and epoxy was studied indifferent ratios by using FTIR and non-isothermal DSC techniques. Compared to other woodadhesives, such as phenol-formaldehyde (PF) or diphenyl methane di-isocyanate, UF resinpossesses some advantages such as fast curing, good performance in the panel, water solubilityand lower price. From the infrared spectra using a peak-height method, which was based on theratio of the height of the characteristic to reference absorbance peak, degree of conversion atdifferent temperature were calculated. FTIR measurements showed decrease in the intensity ofthe absorption band of epoxide group at 916 cm-1 during curing process. At all temperature, thedegree of conversation increased when the intensity of the band at 916 cm-1 decreased.The rate of epoxide conversion depends on the weight ratio of adhesives and also on thetemperature of cure reaction. In general, the results obtained from isothermal DSC experimentsshowed that the rate of reaction is proportional to the heat flow. A higher isothermal temperatureand higher urea formaldehyde concentration led to increase in the reaction rate.کلیدواژه ها
Curing Reaction, PB, DSC Analysis, FTIR, Adhesiveمقالات مرتبط جدید
- Molecular Simulation of Water Transport through Polyamide Membrane in K+Cl- Salt Solution
- نانوکامپوزیت ها در دندانپزشکی
- Improving the characteristics of L-shaped graphene-based gas sensor using gold block on the surface
- Molecular Modelling of Gelatin Bundles for Atomistic Investigations Suggesting Two Stable Conformations
- بررسی تاثیر نانوذرات منیزیم بر جوانه زنی بذر و رشد گیاهچه بادرنجبویه Melissa officinalis
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.