Microstructural Characterization and Modeling of Discontinuously Reinforced Al-matrix Composite
- سال انتشار: 1386
- محل انتشار: دومین کنفرانس بین المللی و هشتمین کنفرانس ملی مهندسی ساخت و تولید
- کد COI اختصاصی: ICME08_135
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1756
نویسندگان
M.Sc.Azad University of South Tehran, Tehran, Iran
Phd-School of Metallurgy and Materials Engineering-University of Tehran, Tehran, Iran
Phd-Malek Ashtar University of Technology, Tehran, Iran
student -School of Metallurgy and Materials Engineering-University of Tehran, Tehran, Iran
چکیده
Aluminum matrix composites are very common engineering materials in automotive, aerospace and other application due to their low weight, high strength, and excellent wear resistance. In this work, different amount of zircon ceramic particles (ZrSiO4) were incorporated in A356.1 (aluminum alloy) by stir-casting route. Processing temperature was 750C. This method was in order to achieve homogeneous composite material and better solidification conditions. SEM micrographs show that reinforcing particles were dispersed homogeneously in the samples (not clustered). The hardness and tensile strength of zircon reinforced aluminum were higher than those of the monolithic aluminum. The hardness and tensile strength were decreased with zircon amount increasing above 5 vol.%.کلیدواژه ها
Aluminum matrix composites, reinforcement, zirconمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.