New possibilities for the masteralloy approach
- سال انتشار: 1397
- محل انتشار: ششمین کنفرانس بین المللی متالورژی پودر
- کد COI اختصاصی: PMAUTO06_084
- زبان مقاله: انگلیسی
- تعداد مشاهده: 445
نویسندگان
Institute of Chemical Technologies and Analytics, Vienna University of Technology
Institute of Chemical Technologies and Analytics, Vienna University of Technology
Atomizing Systems Limited, Sheffield, England
Institute of Chemical Technologies and Analytics, Vienna University of Technology
چکیده
The Masteralloy (MA) alloying route has a great potential for reducing the alloying costs in sintered steels, while allowing the introduction of innovative alloying systems. However, in order to achieve an efficient use of the alloying elements, the particle sizes needed are often below 25 µm, which means that for standard gas atomization a significant fraction of the batch has to be discarded. This work evaluates the performance of steels containing MA powders obtained with a novel atomization technique (Ultra-High-Pressure Water atomization) that allows the production of low-cost powders with low oxygen contents, rounded morphologies and mean particle sizes as low as 6 microns. Mechanical properties, dimensional variations and interstitial contents were measured in steels containing different MA compositions sintered at either 1120 °C or1250 ºC in N2-5H2 atmospheres. With less than 3 wt.% of alloying elements these steels present excellent combinations of properties, reaching strength levels between 560-915 MPa and hardness 220-260 HV10, combined with elongations of 1.3-3.2% and impact energies around 20-30 J/cm2.کلیدواژه ها
Lean low alloy steels, Alloying design, Masteralloys, Mechanical propertiesمقالات مرتبط جدید
- مطالعه تجربی و مقایسه رفتار مکانیکی گلار۱/۲ و گلار ۲/۳ تحت بار خمشی
- Investigation effect of process parameters of Al۶۰۶۱ composites fabricated by FSP on microstructure, mechanical properties with minitab and designexpert
- بررسی خواص جوشمان های سطحی دو لایه بر روی ورق فولادی دو لایه
- مکانیزم ها در دیگ های بخار
- Numerical Study on the cavitation patterns in a Francis turbine
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.