An investigation on structural properties of pure Al foam manufactured by powder metallurgy using TiH2 foaming agent
- سال انتشار: 1396
- محل انتشار: ششمین کنفرانس بین المللی مهندسی مواد و متالورژی و یازدهمین همایش ملی مشترک انجمن مهندسی متالورژی و مواد ایران و انجمن علمی ریخته گری
- کد COI اختصاصی: IMES11_295
- زبان مقاله: انگلیسی
- تعداد مشاهده: 372
نویسندگان
MSc in materials engineering Department of Materials Engineering,Ferdowsi University of Mashhad, Mashhad, Iran
Professor in materials engineering Department of Materials Engineering,Ferdowsi University of Mashhad, Mashhad, Iran
چکیده
Aluminum foams are a new generation of materials and have unique features and considerable applications in the manufacturing industry. In this research, Al foams were produced with titanium hydride as foaming agent by powder metallurgy method. Amounts of TiH2 powder were 0.5, 1 and 2 wt. %. Partial sintering was performed at 400 °C and foaming temperatures were changed from 750 °C to 850 °C. The effects of foaming agent weight percent and heating parameters were investigated by comparing structural properties of final foams. Macroscopic examinations showed that foams containing 1 wt. % TiH2 manufactured at 800°C have 77.8% porosity with the most uniform structure.کلیدواژه ها
Aluminum foam, Powder metallurgy, Titanium hydride, Porosityمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.