The Investigation of Optical and Morphological Properties of CdSe Quantum Dots coated on the Forsterite Nanoparticles Substrate Synthesized by Combustion Sol-Gel Method
- سال انتشار: 1396
- محل انتشار: ششمین کنفرانس بین المللی مهندسی مواد و متالورژی و یازدهمین همایش ملی مشترک انجمن مهندسی متالورژی و مواد ایران و انجمن علمی ریخته گری
- کد COI اختصاصی: IMES11_007
- زبان مقاله: انگلیسی
- تعداد مشاهده: 306
نویسندگان
Department of Materials Science and Engineering, Sharif University of Technology, Tehran, Iran
Department of Nanomaterials and Nano coatings, Institute for Color Science and Technology, Tehran, Iran
Department of Nanomaterials and Nano coatings, Institute for Color Science and Technology, Tehran, Iran
چکیده
In the synthesis of quantum dots, quantum yied is always important. Furthermore, this definition depends nt factorsdepends favtors, such as particle saze, concentration, and temperature. compounds is the presence of oxygen during synthesis. To prevent the formation of oxide compounds in the synthesis of quantum dots, controlled atmospheres are used. On the other hand, the application of quantum dots in labeling of bioscience is using widely in medicine and therapy of cancer cells. In the new method, CdSe quantum dots were coated on ceramic nanoparticles of forsterite, which is synthesized by the sol-gel combustion method and without presence of controlled of the atmosphere. The results obtained from the X-ray diffraction pattern represent the synthesis of the forsterite phase without impurities and segregation. After applying quantum dots on the substrate, the emission range of forsterite nanoparticles was shifted from blue to yellow. Moreover, Quantum yield of quantum dots was more than the samples, which did not be coated. Images of TEM reveal the quantum dots coated on Forrester nanoparticles in size of 5 to 7 nm. In addition, the images obtained from SEM showed agglomerated Forrester nanoparticles, in size of 200 nm. The mechanism of this synthesis is according to the creation of a high range order of quantum dots on substrate of forsterite nanoparticles.کلیدواژه ها
CdSe Quantum dot, forsterite Nano particles, luminescent composite, Combustion processمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.