FABRICATION OF NANOSTRUCTURED Ni-C SOLD SOLUTION ALLOYS BYMECHANICAL ALLOYTNG
- سال انتشار: 1390
- محل انتشار: سومین کنفرانس بین المللی مواد فوق ریزدانه و نانوساختار
- کد COI اختصاصی: UFGNSM03_192
- زبان مقاله: انگلیسی
- تعداد مشاهده: 296
نویسندگان
Department of Materials and Metallurgy Engineering, Iran University of Science & Technology, Narmak, Tehran, Iran
Institute of Plasma Physics and Nuclear Fusion, Amir Abad, Tehran, Iran
Department of Materials and Metallurgy Engineering, Iran University of Science & Technology, Narmak, Tehran, Iran
چکیده
Cu and Ni elemental powder mixtures containing 25, 50, and 75 at% Cu. were subjected to mechanical alloying (MA) in a planetary ball mill under various milling times. The structural evolution during mechanical alloying was characterized by means of X-ray diffractometry (XRD) and scanning electron microscopy (SEM). Experimental results indicate that nano-structured solid solution with single-phase and homogeneous distribution of Ni and Cu has been prepared through interdiffusion mechanism. Average crystallite size of as-milled powders was decreased with increasing Ni content and increasing milling time, and found to be in the order of 15-40 nm after 30 h of milling for all powder compositions. Moreover, lattice constant and lattice strain of solid solutions were increased during mechanical alloying.کلیدواژه ها
Mechanical Alloying, Nano-Structured, Solid Solution, Ni-Cu Binary Alloysمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.