THE EFFECT OF CURRENT DENSTY ON CORROSION BEHAVOR OF PULSE ELECTRODEPOSTED N-SCNANOCOMPOSITE COATING ON AZ91 MAGNESUMALLOY
- سال انتشار: 1390
- محل انتشار: سومین کنفرانس بین المللی مواد فوق ریزدانه و نانوساختار
- کد COI اختصاصی: UFGNSM03_123
- زبان مقاله: انگلیسی
- تعداد مشاهده: 384
نویسندگان
School of Metallurgy di Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
School of Metallurgy & Materials Engineering, College of Engineering, University of Tehran, Tehran, Iran
چکیده
Magnesium and its alloys are the lightest of structural metals, which makes them one of the most promising materials to minimize vehicle weight, but poor surface properties restrict the application of these alloys. Toimprove the surface properties of AZ91 magnesium alloy, Ni-SiC nanocomposite coating was applied by pulse electrodeposition. The effect of current density, in the range of 20-90 mA/cm , on corrosion behavior of AZ91 was investigated. The morphology and phase analysis of the coatings were studied using Scanning Electron Microscopy (SEM) and X-Ray Difraction (XRD) analysis, respectively. The corrosion behavior of the coated AZ91 alloy was investigated by potentiodynamic polarization. Microhardness measurement of the coatingsshowed a 347% enhancement. The results also revealed a significant improvement in corrosion resistance, that is, the corrosion current density decreased from 2.69 mA/cm for uncoated specimen to 0.003 mA/cm the sample coated at current density of 90 mA/cm and the corrosion potential increased from -2.069 V for uncoated specimen to -0.07 V for the sample coated at current density of 90 mA/cm.کلیدواژه ها
Ni-SiC, nano-composite coating, pulse electrodeposition, corrosion current density, corrosionpotentialمقالات مرتبط جدید
- مطالعه تجربی و مقایسه رفتار مکانیکی گلار۱/۲ و گلار ۲/۳ تحت بار خمشی
- Investigation effect of process parameters of Al۶۰۶۱ composites fabricated by FSP on microstructure, mechanical properties with minitab and designexpert
- بررسی خواص جوشمان های سطحی دو لایه بر روی ورق فولادی دو لایه
- مکانیزم ها در دیگ های بخار
- Numerical Study on the cavitation patterns in a Francis turbine
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.