Optimization of Nano-crystalline Gamma Al2O3 Powders Preparation Using Taguchi L-4 Method
- سال انتشار: 1387
- محل انتشار: دوازدهمین کنگره ملی مهندسی شیمی ایران
- کد COI اختصاصی: NICEC12_700
- زبان مقاله: انگلیسی
- تعداد مشاهده: 1668
نویسندگان
Chemical Engineering Department, Amirkabir University of Technolog
Chemical Engineering Department, Amirkabir University of Technology
چکیده
Nano-structured gamma Al2O3 powders were prepared by combustion synthesis method utilizing serine as complexing agent. The product was sonicated to obtain nano powders. A Taguchi L-4 statistical design of combustion synthesis utilized to optimize the production of gamma-alumina powder. The product was characterized by XRD, BET, SEM, and LLS. Nano crystalline γ-alumina with crystal size between 4.26nm to 5.47nm and α-alumina powders with crystal size 24.51nm and 28.62nm were obtained by combustion synthesis. The specific surface area was measured by BET method. Result shows 75.21m2/g. The average particle size after sonication of product, observed by LLS, was 79.32 nm.کلیدواژه ها
Aluminum oxide, combustion synthesis, nano-crystal, Serine, Taguchi designمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.