Determination of electro spun PVDF characteristics for relevant study on performance of membrane distillation
- سال انتشار: 1395
- محل انتشار: دوازدهمین سمینار بین المللی علوم و تکنولوژی پلیمر
- کد COI اختصاصی: ISPST12_168
- زبان مقاله: انگلیسی
- تعداد مشاهده: 505
نویسندگان
Amirkabir University of Technology, Department of Textile Engineering, Hafez Avenue, Tehran, Iran
Amirkabir University of Technology, Department of Textile Engineering, Hafez Avenue, Tehran, Iran
Amirkabir University of Technology, Department of chemical Engineering, Hafez Avenue Tehran, Iran
Amirkabir University of Technology, Department of chemical Engineering, Hafez Avenue Tehran, Iran
چکیده
Taking into consideration that the polymer concentration have the significant effect on the resultant nanofiber diameter and electrospun nanofibrous membrane (ENM) structure, this study aims to investigate direct contact membrane distillation (DCMD) performance of the single layer and triple layer polyvinilyden fluoride ENM. The bead-free nanofiber with diameter of 240nm obtained at 20 wt% concentration of polymer solution and increasing PVDF concentration lead to an increase of fiber diameter to 464nm. Results of DCMD operation show the permeate flux of triple layer ENM that has nanofiber with thicker diameter in its middle layer is better than single layer ENM that was obtained from electrospinning of 20 wt% polymer solution.کلیدواژه ها
Membrane distillation-Electrospinning- Polyvinylidene fluoride- Nanofiber membranesdiameter gradientاطلاعات بیشتر در مورد COI