Microstructure evolution of GZ61 alloy in rolling and extrusion processes
- سال انتشار: 1395
- محل انتشار: دهمین همایش مشترک و پنجمین کنفرانس بین المللی انجمن مهندسی مواد و متالورژی و انجمن علمی ریخته گری ایران
- کد COI اختصاصی: IMES10_295
- زبان مقاله: انگلیسی
- تعداد مشاهده: 392
نویسندگان
MSc student, School of Metallurgy and Materials, College of Engineering, University of Tehran
Professor of School of Metallurgy and Materials, College of Engineering, University of Tehran, Tehran, Iran
Assistant Professor of School of Metallurgy and Materials, College of Engineering, University of Tehran, Tehran, Iran
چکیده
This work carried out to investigate the effect of extrusion and rolling process on the microstructure of Mg-Gd-Zn (GZ61) alloys. The samples were examined by using optical microscopy (OM) to evaluate the modification efficiency of the extrusion and rolling treatment. Experimental results show that the microstructures of the as-cast Mg-6%Gd-1%Zn alloy consists of α-Mg and Mg5Gd phases with network structure. But by applying extrusion process, It is apparent that the necklace DRX is responsible for significant grain refinement. As compared to the microstructure of hot rolled and extruded specimens, it can be concluded that mechanical twinning rarely can be seen in extruded alloy. However, The resulting microstructure of hot rolled is showing equiaxed grains with considerable amount of mechanical twinsکلیدواژه ها
Magnesium alloys; Rare earth alloys and compounds; Microstructure; homogenizing tretmentمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.