Synthesis and characterization of soluble polyanline for Corrosion Protection of Carbon steel
- سال انتشار: 1394
- محل انتشار: یازدهمین سمینار سالانه الکتروشیمی ایران
- کد COI اختصاصی: ELECTROCHEMISTRY011_010
- زبان مقاله: انگلیسی
- تعداد مشاهده: 332
نویسندگان
Department of Chemistry, Khajeh Nasir Toosi University of Technology, Tehran, Iran
Mohammad Hamed Barzegar Khaleghi
Department of Chemistry, Khajeh Nasir Toosi University of Technology, Tehran, Iran
چکیده
Polyaniline (PANI) is a unique member of conducting polymers family due to its excellent mechanical and chemical properties [1]. These unique properties made PANI a suitable candidatefor different technological applications such as corrosion protection of metals [2].Despite its good characteristics PANI has the drawback of poor processability and solubility in commonly used organic solvents. This limits the application of PANI to its full potential [3]. In this work aneasily soluble PANI was formed via emulsion synthesis method. In this method different amounts of Dodecylbenzenesulfonic acid (DBSA) was used as emulsifying agent. In this procedureoptimized concentrations of aniline (0.5 M) and DBSA (0.1 M) were dissolved in 50 ml ofchloroform and vigorously stirred. 30 minute later 50 ml solution containing phosphoric acid (1 M) and ammonium persulfate (0.6 M) was slowly added to previous solution. Stirring wascontinued for 1 hour in room temperature. After that a green PANI containing DBSA was formedin the solution. The solvents were evaporated in an oven over night and obtained PANI-DBSA powder was thoroughly washed with deionized water. This green powder was first characterizedusing Energy-dispersive X-ray spectroscopy (edx) and X-ray diffraction spectroscopy (XRD) andthen used to formulate an anti corrosion coating based on epoxy resin matrix and xylene as a solvent for epoxy resin. Different carbon steel samples were prepared using this formulationincluded bare carbon steel electrodes, electrodes with epoxy coating and electrodes with differentpercent of PANI-DBSA in resin matrix. Corrosion protection performance of samples was investigated in a three electrode cell containing Ag/AgCl and platinum disk as reference andcounter electrode respectively in NaCl 3.5% as electrolyte solution. These test proved that PANIDBSA has high potential in corrosion protection of carbon steel. As it can be seen in Fig.1 Tafel polarization showed a 0.2 V potential change toward more noble potentials in case of 0.1 gr ofPANI-DBSA mixed with 3.6 gr of resin. Electrochemical impedance spectroscopy was also used to evaluate coatings performance. The results showed a relatively smooth surface with very high resistance is formed on carbon steel electrodes. In conclusion we prepared and examined a processable PANI derivate with good corrosion protection performanceکلیدواژه ها
Emulsion synthesis PANI-DBSA, Epoxy resin, Corrosion protection, Carbon steelمقالات مرتبط جدید
- ؛ GRP-۷۸ سنتز و بهینه سازی نانوکامپوزیت آهن نیکل جهت تخلیض ایمونوگلوبولین
- نانوکامپوزیت مبتنی بر کربوکسی متیل سلولز: یک ماده زیستی امیدوار کننده برای کاربردهای زیست پزشکی
- Multi component Reaction of Isoquinoline, Dialkyl acetylenedicarboxylate, Aldehydes and Dimedone Catalyzed by Bio-CuO-NPs
- Synthesize of forward osmosis membrane with Zinc Oxide interlayer for enhanced water desalination
- Co-doping effects in CdWO۴ scintillator thin film as alpha counters: Ag and Gd case
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.