Effect of Rolling Process on Mg/SiC Magnesium Matrix Composites
- سال انتشار: 1394
- محل انتشار: کنفرانس دو سالانه بین المللی مکانیک جامدات تجربی
- کد COI اختصاصی: WMECH03_133
- زبان مقاله: انگلیسی
- تعداد مشاهده: 534
نویسندگان
M.Sc. Student,School of Mechanical Engineering, Iran University of Science and Technology, Tehran, 16846-13114, Iran
Ph.D. Student,School of Mechanical Engineering, Iran University of Science and Technology, Tehran, 16846-13114, Iran
ProfessorSchool of Mechanical Engineering, Iran University of Science and Technology, Tehran, 16846-13114, Iran
چکیده
In this paper, Mg composite containing SiC reinforcement particle has been fabricated using powder metallurgy (PM) process followed by hot rolling. First, 5 and 10 wt. % SiC powder (with average size of 15μm) has been added to Mg powder. Then they have been mixed by using high energy planetary ball-milling under argon atmosphere. In order to fabricate Mg/SiC composite, the mixture has been cold-compacted, sintered and finally hot-rolled in different temperatures and different number of passes. Microstructure and micro-hardness of the samples are investigated by optical microscopy and micro-Vickers hardness test, respectively. Microscopic evaluation of the hot-rolled composites shows a uniform distribution of SiC particles. No significant grain refinement is observed in the composite in comparison to monolithic Mg sample, while the hardness of samples has been increased by enhancing the number of rolling passes and SiC weight fraction.کلیدواژه ها
Magnesium Matrix Composite, Mg/SiC, Powder Metallurgy, Rollingمقالات مرتبط جدید
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.