Martensite Volume Fraction Effect on the Dual-Phase SteelWork Hardening Behavior

سال انتشار: 1394
محل انتشار: کنفرانس دو سالانه بین المللی مکانیک جامدات تجربی
کد COI اختصاصی: WMECH03_058
زبان مقاله: انگلیسی
تعداد مشاهده: 547

نویسندگان

Postgraduate Students of Advanced Materials Research Center, Faculty of Materials Engineering, NajafabadBranch, Islamic Azad University, Najafabad, Isfahan, Iran

M Mansouri

Postgraduate Students of Advanced Materials Research Center, Faculty of Materials Engineering, Najafabad

چکیده

The present study was aimed to evaluate the dual-phase (DP) steels work hardening behavior in terms of Holloman analysis. Low carbon steel (LCS) was annealed at various temperatures of 780, 800, 820 and 840°C in the Muffle urnace and the effect of the martensite volume fraction (VM) on DP steels work hardening behavior was investigated. The Results revealed that the VM increased from 31% to 66% with increasing annealing temperature from 780 to 840°C. The results of the work hardening mechanism in DP steels showed that with more than 66%VM two stages work hardening occurs and with less than (VM=31, 49 and 55%) one stage took place and the work hardening exponent increased with increasing Vm. Relationship between the VM and carbon content was evaluated by mixture rule and the result indicated that martensite W% decreases from 0.42 to 0.2. with increasing the temperature from 780 to 40°C.Moreover, Elongation and ratio of yield stress to tensile strength decreased with increasing VM.

کلیدواژه ها

DP steels, heat treatment, martensite volume fraction, Holloman analysis, mixture rule

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.