Investigation of Mixed-Mode Interlaminar Fractureof Woven Glass Epoxy Composite

سال انتشار: 1393
محل انتشار: چهارمین کنفرانس بین المللی کامپوزیت
کد COI اختصاصی: COMPOSIT04_062
زبان مقاله: انگلیسی
تعداد مشاهده: 740

نویسندگان

Department of Mechanical Engineering, College of Engineering, Bonab Branch, Islamic Azad University, Bonab, Iran

Associate Professor, Department of Mechanical Engineering, Sahand University of Technology, Sahand, Tabriz, Iran

چکیده

In this paper experimental and numerical investigation of the interlaminar fracture behavior of woven glassepoxy composite is performed under static mixed-mode loading, using a specially developed fixture. Woven glass/epoxy composite sheet were produced by hand lay-up method and post-cured in an autoclave set. Butterfly samples wereprepared by saw water machine. Mixed-mode fracture tests from pure mode I to pure mode II were performed. By using of the finite-element simulations were done by ABAQUS, non-dimensional stress intensity factors of butterflysample were computed and a polynomial fit was proposed to evaluate the stress intensity factors of an interlaminar crack subjected to various mixed-mode loadings using new designed fixture. The results show that the composite material used in this study is tougher in shear loading conditions and weaker in tensile loadings.

کلیدواژه ها

Interlaminar mixed-mode fracture, New loading device, Stress intensity factor, Woven composite

مقالات مرتبط جدید

اطلاعات بیشتر در مورد COI

COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.

کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.