Electrospinning of PLA for tissue engineering: Effect of operational parameters on fiber diameters
- سال انتشار: 1390
- محل انتشار: هفتمین کنگره ملی مهندسی شیمی
- کد COI اختصاصی: ICHEC07_441
- زبان مقاله: انگلیسی
- تعداد مشاهده: 853
نویسندگان
Department of Chemical Engineering, Faculty of Engineering, University of Tehran, Tehran, Iran Department of Tissue Engineering, Research Center for New Technologies in Life Science Engineering, University of Tehran, Tehran, Iran
Department of Chemical Engineering, Faculty of Engineering, University of Tehran, Tehran, Iran Department of Tissue Engineering, Research Center for New Technologies in Life Science Engineering, University of Tehran, Tehran, Iran
Department of Chemical Engineering, Faculty of Engineering, University of Tehran, Tehran, Iran Department of Tissue Engineering, Research Center for New Technologies in Life Science Engineering, University of Tehran, Tehran, Iran
Department of Chemical Engineering, Faculty of Engineering, University of Tehran, Tehran, Iran Department of Tissue Engineering, Research Center for New Technologies in Life Science Engineering, University of Tehran, Tehran, Iran
چکیده
Development of tissue engineering scaffold has recently focused on the use of electrospun biocompatible polymers. In this article nonofibers were successfully fabricated from PLA via electrospinning. Important electrospinning. parameters such as solvent, concentration of PLA solutions and electric field intensity were examined to investigate the effects on morphology of the PLA nanofibers. PLA was not soluble in DMF and electrospinning of it in THF and Chloroform/THF (3:1) was not favorable. By DMF addition to chloroform, conductivity increased and the average diameter of the fibers decreased from 3080nm to 524nm. In invistigation of the effect of concentration, by increasing the PLA concentration above 10%, beads-free and continuous fibrers were obtained. The average fiber diameter generally increased from 524nm to 960nm when the concentrations of PLA solution increased from 10% to 15% due to higher viscosity resisting the extension of the jet. Also it was indicated that by increasing voltage could lead to fiber with small diameter and uniform distribution. SEM images of 15% PLA have shown that when the voltage increased from 15 kV to 25 kV, average diameters of the fibers decreased from 1024 nm to 760 nmکلیدواژه ها
Tissue engineering, Scaffold, Electrospinning, Poly(L-lactide), operational parametersمقالات مرتبط جدید
- بررسی وامکان سنجی حذف میکروارگانیسم های ورودی به واحد اسمز معکوس از طریق دستگاه التراسونیک
- The prediction of the amount of salt sediment in the electrolytesolutions with the extended equation of states based on PengRobinson equation of state
- تحلیل و بررسی کارکردها، مزایا و معایب پیشران های مایع، جامد و ترکیبی
- امکان سنجی حفاری جهت دار به همراه دستگاه رزونانس مغناطیسی هسته ای در چاه نگاری
- مدلسازی ژئومکانیکی جهت مقابله با ریزش دیواره چاه های نفت با استفاده از داده های چاه نگاری
اطلاعات بیشتر در مورد COI
COI مخفف عبارت CIVILICA Object Identifier به معنی شناسه سیویلیکا برای اسناد است. COI کدی است که مطابق محل انتشار، به مقالات کنفرانسها و ژورنالهای داخل کشور به هنگام نمایه سازی بر روی پایگاه استنادی سیویلیکا اختصاص می یابد.
کد COI به مفهوم کد ملی اسناد نمایه شده در سیویلیکا است و کدی یکتا و ثابت است و به همین دلیل همواره قابلیت استناد و پیگیری دارد.